Abstract
Thermomigration experiments were conducted to study the change in mechanical properties of 95.5Sn–4Ag–0.5Cu (SAC405) lead-free solder joint under high temperature gradients. This paper presents some observations on samples that were subjected to 1000°C/cm thermal gradient (TG) for 286 h, 712 h, and 1156 h. It was observed that samples subjected to thermal gradient did not develop a Cu3Sn intermetallic compound (IMC) layer, and we observed disintegration of Cu6Sn5 IMC. On the other hand, samples subjected to isothermal annealing exhibited IMC growth. In samples subjected to thermomigration, near the cold side the Cu concentration is significantly higher compared with hot side. Extensive surface hardness testing showed an increase in hardness from the hot to cold sides, which possibly indicates that Sn grain coarsening is in the same direction.
Subject
Electrical and Electronic Engineering,Computer Science Applications,Mechanics of Materials,Electronic, Optical and Magnetic Materials
Reference37 articles.
1. Ye, H.
, 2004, “Mechanical Behavior of Microelectronics and Power Electronics Solder Joints Under High Current Density: Analytical Modeling and Experimental Investigation,” Ph.D. thesis, State University of New York at Buffalo.
2. Damage Mechanics of Microelectronics Solder Joints Under High Current Densities;Ye;Int. J. Solids Struct.
3. A Thermodynamic Model for Electrical Current Induced Damage;Basaran;Int. J. Solids Struct.
4. Failure Modes of Flip Chip Solder Joints Under High Electric Current Density;Basaran;ASME J. Electron. Packag.
5. Thermomigration in SnPb Composite Flip Chip Solder Joints;Huang;Appl. Phys. Lett.
Cited by
28 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献