Reliability of 4H-SiC (0001) MOS Gate Oxide by NO Post-Oxide-Annealing

Author:

Xu Heng Yu1,Wan Cai Ping2,Ao Jin Ping1

Affiliation:

1. Tokushima University

2. Chinese Academy of Sciences

Abstract

In this work, we investigated the oxide reliability of 4H-SiC (0001) MOS capacitors, the oxide was fabricated about 60 nm by thermal oxidation temperature at 1350°C, the oxides than annealed at different temperatures and times in diluted NO (10% in N2). The 4H-SiC MOS structure was analyzed by C-V and I-V measurement. Compared the J-E curves and Weibull distribution curves of charge-to-breakdown for fives samples under different annealing temperature and time, it shows that the high annealing temperature improves the electrical properties as the lifetime enhanced. The mode value of field-to-breakdown (EBD) for thermal oxides by post-oxide-annealing in NO for 30 min at 1350°C was 10.09 MV/cm, the charge-to-breakdown (QBD) of this sample was the highest in all samples, and the QBD value at 63.2% cumulative failure rate was 0.15 C/cm2. The QBD of the sample annealing at 1200°C for 120 min was 0.06 C/ cm2. The effects of NO annealing in high temperature enhance the lifetime of electrical properties and field-to-breakdown obviously. It can be demonstrated that the annealing temperature as high as 1300°C for 30 min can be used to accelerate TDDB of SiC MOS gate oxide.

Publisher

Trans Tech Publications, Ltd.

Subject

Mechanical Engineering,Mechanics of Materials,Condensed Matter Physics,General Materials Science

Cited by 7 articles. 订阅此论文施引文献 订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3