Comparative study on characteristics of Si-based AlGaN/GaN recessed MIS-HEMTs with HfO2 and Al2O3 gate insulators*

Abstract

Two types of enhancement-mode (E-mode) AlGaN/GaN metal–insulator–semiconductor high-electron-mobility transistors (MIS-HEMTs) with different gate insulators are fabricated on Si substrates. The HfO2 gate insulator and the Al2O3 gate insulator each with a thickness of 30 nm are grown by the plasma-enhanced atomic layer deposition (PEALD). The energy band diagrams of two types of dielectric MIS-HEMTs are compared. The breakdown voltage (V BR) of HfO2 dielectric layer and Al2O3 dielectric layer are 9.4 V and 15.9 V, respectively. With the same barrier thickness, the transconductance of MIS-HEMT with HfO2 is larger. The threshold voltage (V th) of the HfO2 and Al2O3 MIS-HEMT are 2.0 V and 2.4 V, respectively, when the barrier layer thickness is 0 nm. The C–V characteristics are in good agreement with the V th’s transfer characteristics. As the barrier layer becomes thinner, the drain current density decreases sharply. Due to the dielectric/AlGaN interface is very close to the channel, the scattering of interface states will lead the electron mobility to decrease. The current collapse and the R on of Al2O3 MIS-HEMT are smaller at the maximum gate voltage. As Al2O3 has excellent thermal stability and chemical stability, the interface state density of Al2O3/AlGaN is less than that of HfO2/AlGaN.