Aluminium incorporation in polar, semi- and non-polar AlGaN layers: a comparative study of x-ray diffraction and optical properties

Abstract

Abstract Growth of AlxGa1−xN layers (0 ≤ x ≤ 1) simultaneously on polar (0001), semipolar ($$10\bar{{\rm{1}}}$$ 10 1 ¯ 3) and ($$11\bar{{\rm{2}}}2$$ 11 2 ¯ 2 ), as well as nonpolar ($$10\bar{{\rm{1}}}0$$ 10 1 ¯ 0 ) and ($$11\bar{{\rm{2}}}0$$ 11 2 ¯ 0 ) AlN templates, which were grown on planar sapphire substrates, has been investigated by metal-organic vapour phase epitaxy. By taking into account anisotropic in-plane strain of semi- and non-polar layers, their aluminium incorporation has been determined by x-ray diffraction analysis. Optical emission energy of the layers was obtained from room-temperature photoluminescence spectra, and their effective bandgap energy was estimated from room-temperature pseudo-dielectric functions. Both x-ray diffraction and optical data consistently show that aluminium incorporation is comparable on the polar, semi- and non-polar planes.