Different Dissociation Behavior of [11-20] and Non-[11-20] Basal Plane Dislocations in 4H-SiС under Electron Beam Irradiation

Abstract

Electron beam induced current (EBIC) and etch pit method have been used to study the dissociation behavior of basal plane dislocations (BPDs) in 4H-SiC under electron beam irradiation. When 20 kV scanning electron beam was applied for 1 h, it has been found that BPDs whose dislocation lines were along [11-20] off-cut direction dissociated into partial dislocations (PDs) forming a stacking fault (SF) between them; while no dissociation was found for BPDs extending along other directions. These results are discussed in terms of different formation energy of SFs expanding from a pure screw type and a mixed type BPD. In addition, the angle between dislocation line of a BPD and the [11-20] off-cut direction might also play a role in determining the minimum energy for SF formation.