Selective area growth of β-Ga2O3 by HCl-based halide vapor phase epitaxy

Abstract

Abstract We demonstrated selective area growth of β-Ga2O3 by HCl-based halide vapor phase epitaxy on SiO2-masked (001) and (010) β-Ga2O3 substrates. Perfect growth selectivity was achieved under the presence of HCl etching gas in addition to the growth precursors. In both substrate cases, (100) facet dominated the grown shapes owing to their smallest surface energy density. High-aspect-ratio structures having (100) sidewall facets were observed for the stripe windows along [010] and [001] directions on the (001) and (010) substrates, respectively. These structures may be applicable to trenches and fins used for β-Ga2O3-based power devices.