Structural Defects in Ion Implanted 4H-SiC Epilayers

Abstract

ABSTRACTTransmission electron microscopy (TEM) was used to investigate Al, Ar, C and Si ionimplanted 4H-SiC epilayers. After the implantation the samples were thermally annealed for 30 minutes at 1700°C. During the annealing process dislocation loops are formed and the generation of such dislocation loops upon annealing, is investigated with respect to dopant electrical activation, peak ion concentration and calculated interstitial/vacancy concentrations. It is concluded that the dislocation loops are generated as the result of a combination of residual damage and excess interstitials generated in a “plus one” (+1) process.