Abstract
ABSTRACTThe defect and atomic profiles for MeV implantation of Si in GaAs were investigated using He++ channeling, TEM, and SIMS. Doses of 1–10 × 1015Si/cm2 at 1–3 MeV were used. MeV implantation at room temperature rendered only a small amount of lattice disorder in GaAs. Upon annealing at 400°C for 1 h or 800°C for 30 a, we observed a ‘defect-free’ surface region (- 1 μ for 3 MeV implant). Below this region, extensive secondary defects were formed in a band which was 0.7 μ wide and centered at 2 μ for 3 MeV implant. These defects were mostly dislocations lying in the [111] plane. SIMS depth profiles of Si implants showed the Si peak to be very close to the peak position of the defects. The experimental profiles of Si were compared to the TRIM calculation; generally good agreement existed among the peak positions.