Micro-Brazing of Stainless Steel Using Ni-P Alloy Plating

Author:

Liu ShubinORCID,Shohji Ikuo,Iioka Makoto,Hashimoto Anna,Hirohashi Junichiro,Wake Tsunehito,Arai Susumu

Abstract

A Ni-P plated layer of 20 μm thickness containing 11 wt.% P was formed on the surface of a stainless steel (SUS304) plate by electroplating. The microstructure and joint strength of the brazed joint with the electroplated Ni-11P layer were investigated. The results indicated that the filler metal was homogeneously distributed between the SUS304 plates and no voids or flaws formed in the brazed filler zone. Fe-Ni-Cr solid solutions were formed at the brazed interface. Moreover, P was mainly concentrated in such brazed filler zone to form P-containing phases. The average shear strength of the brazed joints was determined to be 47.3 MPa. The results demonstrated that the brazing of SUS304 plates using the electroplated Ni-11P layer as the filler metal was successfully realized.

Publisher

MDPI AG

Subject

Fluid Flow and Transfer Processes,Computer Science Applications,Process Chemistry and Technology,General Engineering,Instrumentation,General Materials Science

Reference19 articles.

1. Brittleness of brazed seam for nickel-based filler metals and its influence factors;Yin;Trans. China Weld. Inst.,1997

2. Solidification phenomena in nickel base brazes containing boron and silicon

3. Comparison of brazed joints made with BNi-1 and BNi-7 nickel-base brazing alloys

4. Brazing of Ni based brazing filler metals and the latest trend;Matsu;Weld. Technol.,2011

5. Development of Cu Brazing Sheet with Cu-P Composite Plating

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3