Microstructure and Properties of SUS304 Stainless Steel Joints Brazed with Electrodeposited Ni-Cr-P Alloy Coatings

Author:

Liu ShubinORCID,Shohji Ikuo,Kobayashi TatsuyaORCID,Osanai Katsuharu,Ando Tetsuya,Hirohashi Junichiro,Wake Tsunehito,Inoue Katsufumi,Yamamoto Hiroki

Abstract

In this study, an amorphous Ni-13.4Cr-11.6P (mass%) alloy coating with a thickness of 30 μm was deposited on the surface of SUS304 stainless steel as a brazing filler metal to conduct brazing. The differential thermal analysis measurements indicate that the electrodeposited Ni-13.4Cr-11.6P alloy has a melting point of approximately 892 °C, which is almost consistent with that of the commercial BNi-7 filler metal. The microstructure, shear strength, and fracture mode of the brazed joint were investigated using an electron probe X-ray microanalyzer, a scanning electron microscope, an optical microscope, and a universal testing machine. The results showed that the brazed filler metal is filled between the SUS304 stainless steel plates without any flaws in the brazed seam. The P-containing phases, i.e., the Cr-P rich phase and the (Ni,Fe)3P phase, were formed in the brazed seam. The shear strength of the brazed joint obtained in this study is 59.0 MPa. The fracture occurs in the brazed filler zone, where the brittle P-containing phases are present. Galvanic current measurement results showed that the brazed Ni-13.4Cr-11.6P alloy coating has a better corrosion resistance than that of the brazed Ni-11P alloy coating, which can be attributed to the formation of a large amount of Ni-Fe solid solution and Cr-P rich phase in the top layer of the brazed Ni-13.4Cr-11.6P alloy coating.

Publisher

MDPI AG

Subject

General Materials Science

Cited by 2 articles. 订阅此论文施引文献 订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3