Formation of Aligned α-Si3N4 Microfibers by Plasma Nitridation of Si (110) Substrate Coated with SiO2

Abstract

Plasma nitridation of an amorphous SiO2 layer on Si (110) substrate can form well-aligned α-Si3N4 crystallites in fibrous morphology. Nitriding is performed at a temperature in the range of 800–1000 °C by using microwave plasma with a gas mixture of N2 and H2. Raman spectroscopy shows the characteristics of an α-Si3N4 phase without other crystalline nitrides. As shown by scanning electron microscopy, the formed α-Si3N4 microfibers on the Si substrate can be in a dense and straight array nearly along with Si <11¯0>, and can have a length over 2 mm with a diameter in the range of 5–10 μm. Structural characterization of scanning transmission electron microscopy in cross section view reveals that the elongated α-Si3N4 crystallites are formed on the surface of the nitrided SiO2/Si (110) substrate without any interlayers between Si3N4 and Si, and the longitudinal direction of α-Si3N4 appears mainly along <112¯0>, which is approximately parallel to Si <11¯0>.