Microstructural Evolution and Mechanical Behavior of TA15 Titanium Alloy Fabricated by Selective Laser Melting: Influence of Solution Treatment and Aging

Author:

Wang Qing1ORCID,Jin Binquan1,Zhao Lizhong1,Liu Xiaolian1,Pan Anjian1,Ding Xuefeng2,Gao Wei2,Song Yufeng2,Zhang Xuefeng1

Affiliation:

1. Institute of Advanced Magnetic Materials, College of Materials and Environmental Engineering, Hangzhou Dianzi University, Hangzhou 310018, China

2. College of Mechanical and Electrical Engineering, Hunan University of Science and Technology, Xiangtan 411201, China

Abstract

In this study, TA15 titanium alloys were successfully prepared using selective laser melting (SLM). The results show that the microstructure of each TA15 specimen is composed of a large number of acicular α’ martensite crystals accompanied by a lot of dislocations and twin structures in the martensite due to non-equilibrium heating and cooling via SLM. After solution treatment and aging treatment, the martensite structure is successfully transformed into a typical duplex structure and an equiaxial structure. When there is an increase in the solution temperature, the size of the equiaxed primary α phase and the elongation of the specimen gradually increases, while the thickness of the layered secondary α phase and the tensile strength of the specimen decreases accordingly. After solution treatment at 1000 °C, the specimens show the best comprehensive mechanical properties, i.e., a high-temperature tensile strength of 715 MPa and a corresponding elongation of 24.5%. Subsequently, an appropriate solution–aging treatment is proposed to improve the high-temperature mechanical properties of SLMed TA15 titanium alloys in aerospace.

Funder

Natural Science Foundation of Zhejiang Province

Publisher

MDPI AG

Subject

General Materials Science,Metals and Alloys

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3