Abstract
To confirm the degradation property of solder joints by substrate surface finish, chip resistors are reflow soldered to organic solderability preservative (OSP) and electroless nickel immersion gold (ENIG) finish substrate in a nitrogen atmosphere using the type 6 Sn-3.0Ag-0.5Cu (SAC305) solder paste. To confirm the electrochemical metallic ion migration (ECM) sensitivity with and without photo solder resist (PSR) ink-coated printed circuit board (PCB), comb patterned test vehicles were prepared by the hot air reflow soldering process in nitrogen atmosphere, and the SAC305 solder paste was printed on the conductor of the ECM test PCB. The ECM test was conducted under high temperature and high humidity conditions of 85℃ and 85% RH, respectively. As a result of measuring the void content of the 2012 chip resistor, the average void content of the OSP substrate was higher than that of the ENIG substrate. The thermal shock test (TST) indicated that the degradation rate of the OSP substrate was higher than that of the ENIG substrate. Microstructure analysis showed that the OSP substrate had more crack propagation and thicker intermetallic compound (IMC) thickness than the ENIG substrate. The ECM test revealed that the substrate with PSR-coated PCB coupon generated more dendrites than that without PSR-coated coupon. Because the PSR coated substrate decreased the moisture absorption into the substrate, moredendritesweredeterminedtobe generated.
Funder
Ministry of Trade, Industry and Energy
Publisher
The Korean Welding and Joining Society
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献