Morphology control in Ni/Ti multilayer neutron mirrors by ion-assisted interface engineering and B4C incorporation

Abstract

The optical contrast and minimum layer thickness of Ni/Ti broadband neutron multilayer supermirrors is usually hampered by an interface width, typically 0.7 nm, caused by nanocrystallites, interdiffusion, and/or intermixing. We explore the elimination of nanocrystallites in combination with interface smoothening by modulation of ion assistance during magnetron sputter deposition of 0.8 to 6.4 nm thick Ni and Ti layers. The amorphization is achieved through incorporation of natural B4C where B and C preferably bond to Ti. A two-stage substrate bias was applied to each layer; -30 V for the initial 1 nm followed by -100 V for the remaining part, generating multilayer mirrors with interface widths of 0.40-0.45 nm. The results predict that high performance supermirrors with m-values as high as 10 are feasible by using 11B isotope-enriched B4C combined with temporal control of the ion assistance.