The new equiatomic scandium transition metal aluminides ScTAl for T = Cr, Ru, Ag, Re, Pt, and Au were obtained by arc-melting of the elements followed by subsequent annealing for crystal growth. The samples were studied by powder and single crystal X-ray diffraction. The structures of three compounds were refined from single crystal X-ray diffractometer data: ScCrAl, MgZn2 type, P63/mmc, a = 525.77(3), c = 858.68(5) pm, R
1 = 0.0188, wR
2 = 0.0485, 204 F
2 values, 13 variables, ScPtAl, TiNiSi type, Pnma, a = 642.83(4), b = 428.96(2), c = 754.54(5) pm, R
1 = 0.0326, wR
2 = 0.0458, 448 F
2 values, 20 variables and ScAuAl, HfRhSn type, P6̅2c, a = 722.88(4), c = 724.15(4) pm, R
1 = 0.0316, wR
2 = 0.0653, 512 F
2 values, 18 variables. Phase pure samples of all compounds were furthermore investigated by magnetic susceptibility measurements, and Pauli-paramagnetism but no superconductivity was observed down to 2.1 K for all of them. The local structural features and disordering phenomena have been characterized by 27Al and 45Sc magic angle spinning (MAS) and static NMR spectroscopic investigations.
Cited by
15 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献
1. Structure, physical and 27Al NMR-spectroscopic properties of the equiatomic compounds of the type REAlRh (RE = Sm, Tb, Dy, Er, and Lu);Zeitschrift für Naturforschung B;2024-08-14
2. Synthesis, Physical, and Magnetocaloric Properties of MgZn2-Type Gd2Al3Rh;Inorganic Chemistry;2024-07-18
3. Searching for Laves Phase Superstructures: Structural and 27Al NMR Spectroscopic Investigations in the Hf–V–Al System;Inorganic Chemistry;2024-04-23
4. Formation of the Sub-oxide Sc4Au2O1–x and the Drastically Negative 27Al NMR Shift in Sc2Al;Inorganic Chemistry;2023-06-02
5. Raman and NMR spectroscopic and theoretical investigations of the cubic laves-phases REAl2 (RE = Sc, Y, La, Yb, Lu);Dalton Transactions;2023