Quantitative x-ray diffraction analysis of strain and interdiffusion in β-Ga2O3 superlattices of μ-Fe2O3 and β-(AlxGa1−x)2O3

Abstract

Superlattices composed of either monoclinic μ-Fe2O3 or β-(AlxGa1−x)2O3 with β-Ga2O3 spacers are grown on (010) β-Ga2O3 substrates using plasma-assisted molecular beam epitaxy. High-resolution x-ray diffraction data are quantitatively fit using commercial dynamical x-ray diffraction software (LEPTOS) to obtain layer thicknesses, strain, and compositions. The strain state of β-(AlxGa1−x)2O3 and μ-Fe2O3 superlattices as characterized using reciprocal space maps in the symmetric (020) and asymmetric (420) diffraction conditions indicates coherent growths that are strained to the (010) β-Ga2O3 lattice. β-(AlxGa1−x)2O3 and μ-Fe2O3 superlattices grown at hotter substrate temperatures result in crystal structures with better coherency and reduced defects compared to colder growths. The growth rate of μ-Fe2O3 is ∼2.6 nm/min at Tsub = 700 °C and drops to ∼1.6 nm/min at Tsub = 800 °C due to increased Fe interdiffusion at hotter substrate temperatures. Scanning transmission electron microscopy data of a μ-Fe2O3 superlattice grown at Tsub = 700 °C confirm that there is significant diffusion of Fe atoms into β-Ga2O3 layers.