Effect of the Crystallinity on the Electromigration Resistance of Electroplated Copper Thin-Film Interconnections

Author:

Kato Takeru1,Suzuki Ken2,Miura Hideo3

Affiliation:

1. Department of Finemechanics, Graduate School of Engineering, Tohoku University, 6-6-11-716, Aoba Aramaki, Aobaku, Sendai, Miyagi 980-8579, Japan e-mail:

2. Fracture and Reliability Research Institute, Graduate School of Engineering, Tohoku University, 6-6-11-716, Aoba Aramaki, Aobaku, Sendai, Miyagi 980-8579, Japan

3. Fracture and Reliability Research Institute, Graduate School of Engineering, Tohoku University, 6-6-11-716, Aoba Aramaki, Aobaku, Sendai, Miyagi 980-8579, Japan e-mail:

Abstract

Dominant factors of electromigration (EM) resistance of electroplated copper thin-film interconnections were investigated from the viewpoint of temperature and crystallinity of the interconnection. The EM test under the constant current density of 7 mA/cm2 was performed to observe the degradation such as accumulation of copper atoms and voids. Formation of voids and the accumulation occurred along grain boundaries during the EM test, and finally the interconnection was fractured at the not cathode side but at the center part of the interconnection. From the monitoring of temperature of the interconnection by using thermography during the EM test, this abnormal fracture was caused by large Joule heating of itself under high current density. In order to investigate the effect of grain boundaries on the degradation by EM, the crystallinity of grain boundaries in the interconnection was evaluated by using image quality (IQ) value obtained from electron backscatter diffraction (EBSD) analysis. The crystallinity of grain boundaries before the EM test had wide distribution, and the grain boundaries damaged under the EM loading mainly were random grain boundaries with low crystallinity. Thus, high density of Joule heating and high-speed diffusion of copper atoms along low crystallinity grain boundaries accelerated the EM degradation of the interconnection. The change of Joule heating density and activation energy for the EM damage were evaluated by using the interconnection annealed at 400 °C for 3 h. The annealing of the interconnection increased not only average grain size but also crystallinity of grains and grain boundaries drastically. The average IQ value of the interconnection was increased from 4100 to 6200 by the annealing. The improvement of the crystallinity decreased the maximum temperature of the interconnection during the EM test and increased the activation energy from 0.72 eV to 1.07 eV. The estimated lifetime of interconnections is increased about 100 times by these changes. Since the atomic diffusion is accelerated by not only the current density but also temperature and low crystallinity grain boundaries, the lifetime of the interconnections under EM loading is a strong function of their crystallinity. Therefore, it is necessary to evaluate and control the crystallinity of interconnections quantitatively using IQ value to assure their long-term reliability.

Publisher

ASME International

Subject

Electrical and Electronic Engineering,Computer Science Applications,Mechanics of Materials,Electronic, Optical and Magnetic Materials

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3