Printability assessment of psyllium husk (isabgol)/gelatin blends using rheological and mechanical properties

Author:

Agarwal Piyush Sunil1,Poddar Suruchi1,Varshney Neelima1,Sahi Ajay Kumar1,Vajanthri Kiran Yellappa1,Yadav Kanchan1,Parmar Avanish Singh1,Mahto Sanjeev Kumar1ORCID

Affiliation:

1. Tissue Engineering and Biomicrofluidics Laboratory, School of Biomedical Engineering, Indian Institute of Technology (Banaras Hindu University), Varanasi, India

Abstract

The primary goal of this study is to highlight the rheological and mechanical properties of a new blend composed of naturally-derived hydrogel materials- psyllium husk (PH) and gelatin (G) for its potential use in three-dimensional (3D) printing technology. The mixtures were prepared at various weight ratios of 100PH, 75PH + 25G and 50PH + 50G. A suitable selection of the printable ink was made based on the preliminary screening steps of manual filament drop test and layer stacking by 3D printing. Printing of the common features such as hexagon and square grids helped evaluating shape fidelity of the chosen ink. Although 50PH + 50G blend was found meeting most of the criteria for an ideal 3D printable ink, rheological and mechanical characterizations have been performed for all the ratios of polymeric blends. This study documents the correlation between various factors of rheology that should be taken into account while categorizing any biomaterial as a printable ink. Yield stress was measured as 18.59 ± 4.21 Pa, 268.74 ± 13.56 Pa and 109.16 ± 9.85 Pa for 50PH + 50G, 75PH + 25G and 100PH, respectively. Similarly, consistency index (K) and flow index (n) were calculated using the power law equation and found as 49.303 ± 4.17, 530.59 ± 10.92, 291.82 ± 10.53 and 0.275 ± 0.04, 0.05 ± 0.005, 0.284 ± 0.04 for 50PH + 50G, 75PH + 25G and 100PH, respectively. The loss modulus (G″) was observed dominating over storage modulus (G′) for 50PH + 50G, that depicts its liquid-like property; whereas storage modulus (G′) was found dominating in case of 75PH + 25G and 100PH, indicating their solid-like characteristics. In addition, the loss tangent value (tan δ) of 50PH + 50G was observed exceeding unity (1.05), supporting its plastic behavior, unlike 75PH + 25G (0.5) and 100PH (0.33) whose loss tangent values were estimated less than unity revealing their elastic behavior. Also, 50PH + 50G was found to have the highest mechanical strength amongst the three blends with a Young’s modulus of 9.170 ± 0.0881 kPa.

Funder

Department of Science and Technology, Ministry of Science and Technology

Publisher

SAGE Publications

Subject

Biomedical Engineering,Biomaterials

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3