ABSTRACT: In this study, the viscoelastic properties of a low-density polyethylene (LDPE) filled with glass beads (GBs) are measured at 150 C by means of a capillary rheometer to identify the effect of the particle size on the melt viscoelasticity. The volume fraction of the GB was 8.4%. The surface of the particles has been treated with a silane-coupling agent and the diameter range was from 4 to 180 mm. The results showed that either the entry pressure drop (Pen) or the entry elongation stress (e) is a linear function of shear stress (w) at the channel wall. The values of both Pen and e of these composite melts are close to each other. This illustrates that the influence of the bead size and its distribution on them is insignificant at low filler concentration. The die-swell ratio (B) increases nonlinearly with an addition of w. When the diameter (d) of the beads is less than 50 mm, B decreases dramatically with an increase of d, especially at low shear stress level, and then it decreases slightly under the given shear stress level.
Subject
Condensed Matter Physics,Ceramics and Composites
Cited by
14 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献