Abstract
The mechanical properties of a material can be positively or negatively affected by its applied or residual stress. In this article, a series of molecular dynamic simulations were adopted to investigate the nanoindentation response of monocrystalline copper under tensile pre-deformation. Nanoindentation simulation under stress-free condition was compared with those under pre-tension strain values of 1.2%, 2.4% and 3.6%. Load–displacement curves with hardness value and recovery rates of total work for nanoindentation based on various tensile pre-deformations were obtained and discussed. It indicated that tensile pre-deformations resulted in a higher potential energy in substrate and a lower external energy will be introduced to realize the same elastic or plastic deformation during indentation. Moreover, the evolution of interior defects during indentation was also observed and analysed. The results showed that tensile pre-strain can influence dislocation nucleation behaviour of material during indentation. This article proposed a special molecular dynamic simulation method to characterize the mechanical properties of the material under tensile pre-deformations via nanoindentation, which gives an effective approach to characterize residual stresses in micro- and nanoscale and will have promising application in mechanical characterization of Microelectro Mechanical Systems devices and structures. Further analysis based on experiments will be done in our further research work.
Funder
Special Project for Development of National Major Scientific Instruments and Equipment
National Natural Science Funds for Excellent Young Scholars
National Natural Science Foundation of China
Project of Jilin Provincial Young Science and Technology Innovation Leading Talent Team
Fund Guiding on Strategic Adjustment of Jilin Provincial Economic Structure Project
Specialized Fund for Jilin Provincial Industrial Innovation Project
Cited by
8 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献