Affiliation:
1. Department of Physics, Shiraz University of Technology, Shiraz, 71555-313, Iran
2. Department of Physics, College of Sciences, University of Isfahan, Isfahan, Iran
Abstract
Indium tin oxide (ITO) thin films have been deposited on glass substrate by DC magnetron sputtering in the presence and absence of oxygen gas flux. Subsequently, some of the samples have been annealed in vacuum or air oven at [Formula: see text]C for 20[Formula: see text]min. The optical, surface morphology and electrical characteristics have been examined by spectrophotometry, atomic force microscope, field emission scanning electron microscopy, four-point probe and Hall effect measurements as a function of argon gas flux, film thickness, deposition rate and substrate temperature. Experimental results indicate that the surface roughness increases by decreasing the argon gas flow rate and deposition rate. The result revealed that the lowest surface roughness of 1.07[Formula: see text]nm is achieved at zero oxygen gas flux, argon gas flow 20[Formula: see text]sccm and deposition rate [Formula: see text] Å/s. We have found that the maximum value of merit figure is related to the argon gas flow rate 30[Formula: see text]sccm. In order to obtain a very smooth surface, finally, the ITO thin films have been processed with alumina polishing solution by ultrasonic method. Our experimental results indicate that surface roughness decreases and merit figure increases after polishing process.
Publisher
World Scientific Pub Co Pte Lt
Subject
Materials Chemistry,Surfaces, Coatings and Films,Surfaces and Interfaces,Condensed Matter Physics
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献