Effect of Mn content on corrosion characteristics of lean Mn TWIP steel

Abstract

It is important that the steel plate is manufactured with a high tensile strength to reduce the weight of the body. It is generally accepted that twinning induced plasticity (TWIP) steel is a special steel with not only a high ductility but also a high-tensile strength compared to general steel. While numerous investigations have been carried out on the TWIP steel with an amount of manganese of at least 20%, the investigation of steel with manganese content of less than 20% has seldom been considered until now. In this study, the TWIP steel with manganese of less than 20% (12Mn, 15Mn and 18Mn TWIP steel) was investigated to determine the corrosion properties using electrochemical method. The 18Mn and 12Mn samples exhibited the best and worst corrosion resistance, respectively. It is suggested that the 18Mn sample forms a stable oxide film on the surface because it contains a larger amount of manganese and aluminum compared to the other samples, and their composition enables the easy formation of the oxide film.