Oxidation Kinetics of Chromium Carbide Coating Produced on AISI 1040 Steel by Thermo-Reactive Deposition Method during High Temperature in Air

Author:

Şen Şaduman1,Ozdemir Ozkan1,Demirkıran A. Sukran1,Şen Uğur1

Affiliation:

1. Sakarya University

Abstract

Oxidation of chromium carbide coating formed on AISI 1040 steel deposited by thermo-reactive deposition method (TRD) has been realized by two stepped reactions. In the initial part of the reactions in the oxidation process, carbon atoms combined with chromium on the outer part of the coating layer react with the oxygen in air, effectively up to 120 min. After that, the chromium atoms react with oxygen in the air and produce Cr2O3phase on the coating layer. The higher the temperature and the longer the treatment time, the more the Cr2O3phases became. The kinetic study was realized for the reactions of carbon and chromium with oxygen, individually. The kinetic study of oxidation was calculated by weight changing of the coated samples at the temperatures of 973 K, 1073 K and 1273 K up to 720 min. We established that the chromium carbide coated steel are characterized by an insignificant increase in the mass in the oxidation period up to 3.5 h, after which the degree of oxidation increases somewhat. The nature of oxidation kinetics for chromium carbide coated steel varies from some mass degrease in the initial period ( 2 h) in connection with the formation of CO and CO2to later mass increase with in connection with the formation of Cr2O3layer. The oxidation resistance of chromium carbide coated steel decrease with an increase in oxidation temperature. The growth rate constant of oxidation of chromium carbide coated steel ranged from 5.13x10-13to-9.617x10-11g4.cm-2s-1in the initial period of oxidation (up to 120 min), while it ranged from 3,163x10-13to 2.188 x10-10g4.cm-2s-1in the second period of oxidation test (over 120 min). The activation energies of oxidation of the chromium carbide coated steel are 185 kJ/mol for the initial period and 215 kJ/mol for the second period.

Publisher

Trans Tech Publications, Ltd.

Subject

General Engineering

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3