Abstract
In order to develop porous ceramics with high strength and corrosion resistance as the support for the preparation of asymmetric ceramic membranes, porous ZrO2-Al2O3 composite is designed and fabricated by adding Zr(OH)4.as sintering aid. The content of Zr(OH)4, the sintering temperature and the bending strength before and after corrosion of the composite are discussed. The results shows that 10wt% ZrO2-10wt% Zr(OH)4 -80wt%Al2O3 composite bar fabricated by cold press with the porosity of 32% can be fabricated in 1550°C for 4 h. The bending strength of the composite is 111.2MPa. After corrosion, the quality lose and the bending strength lose is no more than 1%. The tubular composite is suit for the preparation of micro-filtration membrane.
Publisher
Trans Tech Publications, Ltd.
Reference9 articles.
1. Huanting Wang, Xingqin Liu, Yong Zhou, Dingkun Peng, Guangyao Meng, Membr. Sci. Technol. (in Chinese) Vol. 17, (1997), p.47.
2. D. Casellas, M.M. Nagl, L. Llanes, M. Anglada, J. Mater. Proc. Technol. Vol. 143-144, (2003) , p.148.
3. Dan Enache, Magalie Roy-Auberger, Karine Esterle and Renaud Revel, Colloids and Surface A: Physicochem. Eng. Aspects Vol. 220, (2003), p.223.
4. H. Mills, S. Blackburn, J. Euro. Ceram. Soc., Vol. 20, (2000) , p.1085.
5. D. J. Green, C. Nader, R. Brezny, Ceram Trans 7 (1990) 345.
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献