Abstract
This work explores the effects of extended epitaxial defects on 4H-SiC power devices. Advanced defect mapping techniques were used on large quantities of power device wafers, and data was aggregated to correlate device electrical characteristics to defect content. 1200 V class Junction Barrier Schottky (JBS) diodes and MOSFETs were examined in this manner; higher voltage 3.3 kV class devices were examined as well. 3C inclusions and triangular defects, as well as heavily decorated substrate scratches, were found to be device killing defects. Other defects were found to have negligible impacts on device yield, even in the case of extremely high threading dislocation content. Defect impacts on device reliability was explored on MOS-gate structures, as well as long-term device blocking tests on both MOSFETs and JBS diodes. Devices that passed on-wafer electrical parametric tests were found to operate reliably in these tests, regardless of defect content.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,Condensed Matter Physics,General Materials Science
Reference9 articles.
1. K. Hamada et al., JJAP, vol. 54, no. 4, pp.4-7, (2015).
2. E. Van Brunt et al., Reliability assessment of a large population of 3.3 kV, 45 A 4H-SIC MOSFETs,, Proc. ISPSD 2017, Sapporo, pp.251-254.
3. Non-destructive Recognition Procedures of Defects in Silicon Carbide Wafers,, JEITA EDR-4712/100, (2016).
4. T. Kimoto and J. Cooper, Fundamentals of Silicon Carbide Technology,, p.161, (2014).
5. Q. Wahab et al., Influence of epitaxial growth and substrate-induced defects on the breakdown of 4H-SiC Schottky diodes,, APL, vol. 76, no. 9, pp.2725-2727, (2000).
Cited by
27 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献