Abstract
High-temperature mechanical properties, machinability, oxidation resistance and thermal shock resistance of different content of carbon particles modified silicon carbide composite ceramics (Cp/SiC) prepared by pressureless sintering techniques were studied. Adhesion of Cp/SiC to melted glass under 1000°C was also observed. The results showed that 15-Cp/SiC had the optimum machinability and it also did not adhere to melted glass at high temperature. And flexural strength, hardness, and fracture toughness of 15-Cp/SiC is 136.5MPa, 274.6kgf/mm2, 2.58MPa•m1/2 respectively. The good performance of Cp/SiC made it possible to be used as high temperature glass fixture, which means that Cp/SiC can not only improve the service life of fixture materials, but also broaden the application fields of SiC ceramics.
Publisher
Trans Tech Publications, Ltd.
Reference10 articles.
1. W. Wesch, Nucl. Instrum. Methods Phys. Res., B Beam Interact. Mater. Atoms 116 (1996) 305.
2. O. Kordina, S.E. Saddow, in: S.E. Saddow, A. Agarwal (Eds. ), Advances in Silicon Carbide Processing and Applications, 2004, p.1, USA, Norwood, MA, (2004).
3. PAN Yusong, XU Yongdong, CHEN Zhaofeng, et al. Ablation properties analysis of 2D C/SiC composites [J]. Ordnance Mater Sci Eng (in Chinese), 2006, 29(1): 17–20.
4. BOITIER G, VICENS J, CHERMANT J L. Understanding the creep behaviorof a 2. 5D C/SiC composite I : morphology and microstructure of the as received material[J]. Materials Science and Engineering, 2000, A279: 73-80.
5. BOITIER G, CHERMANT J L, VICENS J. Understanding the creep behavior of a 2. 5D C/SiC compositeⅡ: experimental specifications andmacroscopicmechanical creep responses [J]. Materials Science and Engineering, 2000, A289: 265-275.
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献