Failure Analysis for Girth Weld of Gathering Pipelines

Abstract

Through failure generalization, fracture feature analysis and material performance test, a comprehensively analysis was made on the fracture failure analysis for girth weld of gathering pipelines containing H2S gas. The results showed that the fracture failure might be mainly due to sulfide stress cracking in the girth weld. The crack originated from the fusion line on the inner surface of girth weld and extended along the girth weld to outside closed to bends. The sulfide stress cracking of the girth weld was caused by the intersection of multiple factors. The service condition was located in SSC 3 zone and the SSC risk of girth weld was high. The girth weld itself was not been stress-relieved, and its ability to resist SSC was poor. Due to low wall thickness, welding defects, welding stress and additional load, the actual stress of weld was higher.