Mechanical and Phase Stability of Zirconia Toughened Alumina

Abstract

The JMM-ZTA, a kind of zirconia-toughened alumina, is a bearing ceramic newly developed for artificial joints. Although it has already been reported that mechanical strength and fracture toughness are higher in the JMM-ZTA than in alumina, the stability of the JMM-ZTA has not been studied in detail yet. In the present study, the stability of the JMM-ZTA with respect to mechanical strength and crystalline phases was examined under hydrothermal environment, and the results were compared with those of alumina. Both the 4-point bending strength and the fraction of monoclinic zirconia unchanged even after the aging test at 121°C for 300 h. These results indicate that the JMM-ZTA possesses quite excellent stability to be used as bearing material of artificial joints.