Abstract
sup>57Fe-enriched BiFeO3 (BFO) thin films were fabricated on SiO2/Si substrates from a stoichiometric precursor solution by chemical solution deposition process. The Bi/Fe molar ratio of the thin films decreased from 0.95 to 0.80 with increase in the sintering temperature. A perovskite phase and flat surface were obtained in the BFO thin films sintered at 500 and 600 °C. However, the 57Fe Mössbauer spectra showed a mixture phase due to amorphous and/or Bi2Fe4O9 phases in the BFO thin films. The valence state of Fe ions of the BFO thin films was confirmed to be only Fe3+ by the Mössbauer spectra.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,General Materials Science
Reference10 articles.
1. K. Y. Yun, D. Ricinschi, T. Kanashima, M. Noda and M. Okuyama: Appl. Phys. Lett. Vol. 89 (2006), p.192902.
2. Y. N. Venevtsev, G. Zhadanov and S. Solon'ev: Sov. Phys. Crystallogr. Vol. 4 (1960), p.538.
3. J. Wang, J. B. Neaton, H. Zheng, V. Nagarajan, S. B. Ogale, B. Liu, D. Viehland, V. Vaithyanathan, D. G. Schlom, U. V. Waghmare, N. A. Spaldin, K. M. Rabe, M. Wuttig and R. Ramesh: Science Vol. 299 (2003), p.1719.
4. H. Uchida, R. Ueno, H. Nakaki, H. Funakubo and S. Koda: Jpn. J. Appl. Phys. Vo. 44 (2005), p. L561.
5. K. Tanaka, Y. Tsukamoto, K. Hayakawa and Y. Yoshida: Jpn. J. Appl. Phys. Vol. 51 (2012), p. 09LB03.
Cited by
4 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献