Abstract
The effect of strain rate on tensile properties of several lead-free solder was investigated using miniature size specimens. High-temperature lead-free solder which are Sn-Cu and Sn-Sb alloys were prepared. Moreover, low-Ag lead-free solder which are Sn-1Ag-0.7Cu (SAC107, mass%) based alloys were prepared. Sn-3Ag-0.5Cu (SAC305) was also prepared for comparison. Tensile strength is proportion to the logarithm of strain rate in all solder investigated. Although 0.1% proof stress decreases at high strain rate in high-temperature solder, it scarcely changes in low-Ag solder. Elongation somewhat increases with increasing strain rate in high-temperature solder. It increases with increasing strain rate in low-Ag solder although it is lower than that of SAC305. Chisel point fracture mainly occurred except Sn-13Sb. In Sn-13Sb, brittle fracture occurred and thus elongation was lower than those of other solder. Sn-8.5Sb and Sn-1Ag-0.7Cu-1Bi-0.2In show mechanical properties similar to SAC305.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,Condensed Matter Physics,General Materials Science
Reference13 articles.
1. J. Bath, Lead-Free Soldering, Springer, New York, (2007).
2. Y. Takaku, I. Ohnuma, Y. Yamada, Y. Yagi, Y. Nishibe, R. Kainuma and K. Ishida, J. Electron. Mater., 35 (2006) 1926-(1932).
3. S. Sakuyama, T. Akamatsu, K. Uenishi and T. Sato, The IEICE Trans. on Electron., J93-C (2010) 485-492.
4. N. Hamada, T. Uesugi, Y. Takigawa and K. Higashi, Mater. Trans., 54 (2013) 796-805.
5. I. Shohji, T. Yoshida, T. Takahashi and S. Hioki, Journal of Materials Science: Materials in Electronics, 15 (2004) 219-223.
Cited by
5 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献