Effect of High Rotating Magnetic Field on the Solidified Structure of Al–7wt.%Si–1wt.%Fe Alloy

Abstract

Al–7wt.-% Si–1wt.-% Fe alloy was solidified unidirectionally in the Crystallizer with High Rotating Magnetic Field (CHRMF). The diameter of sample was 8 mm and its length was 120 mm. The parameters of solidification were as follows: solid/liquid interface velocity ~0.082 mm/s, temperature gradient 7+/-1 K/mm, magnetic induction 0 and 150 mT, frequency of magnetic field 0 and 50 Hz. The structure solidified without rotating magnetic field (RMF) showed a homogeneous, columnar dendritic one. The structure solidified by using magnetic stirring showed a dual periodicity. On the one hand, the branches of the “Christmas tree”-like structure known from the earlier experiments contained Al+Si binary eutectic. On the other hand, bands with higher Fe- and Si-content formed in the sample, which were at a larger distance from each other than the branches of the “Christmas tree” structure. The developed microstructure was analyzed by SEM with EDS. The average Si- and Fe-concentrations were measured on the longitudinal section at given places along the length of sample. Furthermore the Si- and the Fe-concentrations close to the bands and among the bands as well as the composition of the compound phases were determined.