Abstract
Using magnetic stirring during solidification provides a good opportunity to control the microstructure of alloys, thus controlling their physical properties. However, magnetic stirring is often accompanied by a change in local concentrations, and new structures form which could harm the physical properties. This research paper investigated the effect of forced melt flow by a rotating magnetic field (RMF) on the macrostructure of an Al-Si eutectic alloy. To serve this purpose, Al-12.6 wt% Si alloy samples were solidified in a vertical Bridgman-type furnace equipped with a rotating magnetic inductor to induce the flow in the melt. The diameter and length of the sample are 8 mm and 120 mm, respectively. The solidification parameters are a temperature gradient (G) of 6 K/m, and the solid/liquid front velocity (v) of 0.1 mm/s. These samples were divided into parts during the solidification process, where some of these parts are solidified under the effect of RMF stirring while others are solidified without stirring. The structure obtained after solidification showed a distinct impact of stirring by RMF; new phases have been solidified which were not originally present in the structure before stirring. Besides the eutectic structure, the new phases are the primary aluminum and the primary silicon. The Si concentration and the volume fraction of each phase were measured using Energy-Dispersive Spectroscope (EDS)and new image processing techniques. The experimental results reveal that applying the RMF during the solidification has a distinct effect on the macrostructure of Al-Si eutectic alloys. Indeed, the RMF provokes macro-segregation, reduces the amount of eutectic structure, and changes the sample’s Si concentration distribution.
Funder
Hungarian National Research, Development, and Innovation Office
European Space Agency
Subject
General Materials Science,Metals and Alloys
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献