Liu Yiqun,Kim Hoon,Wang Jun-Jieh,Li Huazhi,Gordon Roy G.
Abstract
Amorphous LaAlO3 films were deposited on hydrogen-terminated silicon substrates by atomic layer deposition (ALD) at 300 oC. The precursors were lanthanum tris(N,N'-diisopropylformamidinate), trimethylaluminum (TMA) and water. Capacitance-voltage measurements made on ALD MoN/LaAlO3/Si stacks showed humps especially at low frequencies. They were effectively removed by O2 treatment at 300 o C without affecting the dielectric constant (κ~15). The O2 treatment can be carried out either after deposition of a LaAlO3 film, or after each ALD cycle. The O2 treatment also lowered the leakage current from 80 mA cm-2 to 1 mA cm-2 for EOT = 1.3 nm. This indicates that oxygen vacancies are the main defects in as-deposited LaAlO3. Oxygen treated LaAlO3 is one of the best candidates for future high-κ dielectric material due to its low leakage, low defect density and abrupt interface with silicon.
Publisher
The Electrochemical Society
Cited by
20 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献