Color stability and surface roughness of ormocer- versus methacrylate-based single shade composite in anterior restoration

Abstract

Abstract Background The blending ability of universal shade composites and their stability in the oral environment are of great concern in restoring anterior teeth. This study aims to evaluate and compare the color stability and surface roughness of two single-shade composite restorations, ormocer-based composite (OBC) and methacrylate resin-based composite (RBC), after storing them in different staining media. Materials and methods In this study, two universal shade composite restorative materials were tested: a nanohybrid OBC (Admira fusion X-tra, Voco) and a supra-nanofilled RBC (Omnichroma, Toukyama). In total, 60 cylindrical centralized cavities (diameter: 5 mm, depth: 2 mm) were prepared in sound extracted-human central incisors and divided into two equal groups according to the restorative material used (n = 30). According to the storage media, the teeth of each group were divided into three subgroups (n = 10): artificial saliva, black tea, and cola. The restoration color was evaluated for all teeth at baseline and after four weeks of storage. The color stability (∆E) was measured using a reflective spectrophotometer (X-Rite, model RM200QC, Neu-Isenburg, Germany). The surface roughness (Ra) was evaluated using three-dimensional optical profilometry (Wyko, Model NT 1100, Veeco, Tucson, USA). Additionally, the extracted data were analyzed using two-way analysis of variance (ANOVA), one-way ANOVA and Student’s t-test. Results In the baseline evaluation, there were no statistically significant differences with respect to color matching or surface roughness results between the two studied restorative materials. However, the differences were statistically significant after storing them in different media. Conclusion Universal composites showed satisfactory color matching with different teeth colors and accepted surface smoothness, whereas the aging procedure exerted a negative effect on their color stability and surface characteristics.