Impact of Long-Term Operation on the Reliability and Durability of Transit Gas Pipelines-Reference-Cited by-同舟云学术

Impact of Long-Term Operation on the Reliability and Durability of Transit Gas Pipelines

Published:2020-04-01 Issue:1 Volume:70 Page:115-126
ISSN:2450-5471
Container-title:Strojnícky časopis - Journal of Mechanical Engineering
language:en
Short-container-title:

Author:

Igor Okipnyi¹,Lyubomyr Poberezhny²,Vasyl Zapukhliak²,Andrii Hrytsanchuk²,Liubov Poberezhna³,Andrij Stanetsky²,Viktoria Kravchenko²,Ihor Rybitskyi²

Affiliation:

1. Ternopil Ivan Puluj National Technical University , Ruska str. 56, Ternopil , Ukraine

2. Ivano-Frankivsk National Technical University of Oil & Gas , Karpatska str. 15, Ivano-Frankivsk , Ukraine

3. Ivano-Frankivsk National Medical University , Galytska str. 2, Ivano-Frankivsk , Ukraine

Abstract

Abstract Corrosion and corrosion-fatigue tests of the material of the pipeline, which was in operation for 41 years. It has been shown that prolonged operation reduces the parameters of resistance to fatigue and prolonged static loading in corrosive environments. It was established that the degradation of physical and mechanical properties is insignificant, Ukraine’s main gas pipelines are ready to operate at full capacity provided that timely monitoring measures are carried out.

Publisher

Walter de Gruyter GmbH

Subject

Mechanical Engineering

Link

https://www.sciendo.com/pdf/10.2478/scjme-2020-0011

Reference18 articles.

1. [1] Maruschak, P. Prentkovskis, O., Bishchak R. “Defectiveness of external and internal surfaces of the main oil and gas pipelines after long-term operation”, Journal of Civil Engineering and Management, 22(2), pp. 279 – 286, 2016. DOI: 10.3846/13923730.2015.110067210.3846/13923730.2015.1100672

2. [2] Bolzon, G., Rivolta, B., Nykyforchyn, H., Zvirko, O. “Mechanical analysis at different scales of gas pipelines”, Engineering Failure Analysis, 90, pp. 434 – 439, 2018.10.1016/j.engfailanal.2018.04.008

3. [3] Meshkov, Y.Y., Shyyan, A.V., Zvirko, O.I. “Evaluation of the in-service degradation of steels of gas pipelines according to the criterion of mechanical stability”, Materials Science 50(6), pp. 830 – 835, 2015.10.1007/s11003-015-9790-3

4. [4] Nykyforchyn, H., Zvirko, O., Tsyrulnyk, O., Kret, N. “Analysis and mechanical properties characterization of operated gas main elbow with hydrogen assisted large-scale delamination”, Engineering Failure Analysis 82, pp. 364 – 377, 2017.10.1016/j.engfailanal.2017.07.015

5. [5] Zhukov, D., Konovalov, S., Afanasyev, A. “Morphology and development dynamics of rolled steel products manufacturing defects during long-term operation in main gas pipelines”, Engineering Failure Analysis 109, 104359, 2020. DOI: 10.1016/j.engfailanal.2019.10435910.1016/j.engfailanal.2019.104359

Cited by 17 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. Evaluating hydrogen embrittlement susceptibility of operated natural gas pipeline steel intended for hydrogen service;Engineering Failure Analysis;2024-09

2. Experimental Studies on the Dynamics of the Movement of Cleaning Pigs Through Tee Pipe Fittings;Strojnícky časopis - Journal of Mechanical Engineering;2024-05-01

3. Development of the methodology for assessing the serviceability of existing gas pipelines of Ukraine under green hydrogen transportation;Procedia Structural Integrity;2024

4. Corrosion modelling of welded joints of wind power facilities;Procedia Structural Integrity;2024

5. Peculiarities of Fatigue Crack Growth in Steel 17H1S after Long-Term Operations on a Gas Pipeline;Materials;2023-04-07