Balitskii Alexander,Ivaskevich Ljubomyr,Mochulskyi Volodymyr,Eliasz Jacek,Skolozdra Oleg
Abstract
Abstract
The effect of hydrogen on short-term strength, low-cycle durability and planestress fracture toughness of 10Cr15Ni27 steel, 04Cr16Ni56 and 05Cr19Ni55 alloys at pressure up to 35 MPa and temperature 293. . . 773 K was investigated. The modes of hydrogen action for which the elongation , reduction of area , low-cycle durability N and crack resistance parameters Kc of alloys are minimal were established: hydrogen pressure above 10 MPa (non-hydrogenated specimens of 04Cr16Ni56 alloy) and above 15 MPa (hydrogenated specimens of 10Cr15Ni27 steel and 05Cr19Ni55 alloy, hydrogen concentration 15 and 19 wppm, respectively).