Author:
Chan V. Z-H.,Rothman J. B.,Palladino P.,Sneddon L. G.,Composto R. J.
Abstract
Excellent quality boron nitride (BN) thin films on silicon have been produced by a simple procedure involving spincoating solutions of the “single-source” polymeric-precursor polyborazylene, (B3N3H∼4)x, on a silicon substrate, followed by pyrolysis at 900 °C. Rutherford backscattering spectrometry (RBS) indicates that the B/N ratios are 1.37 and 1.09 for conversions carried out in a vacuum oven at 900 and 1250 °C, respectively. Forward recoil spectrometry (FRES) showed that the atomic percent of residual hydrogen is 10 and 9%, respectively. Plain-view and cross-sectional scanning electron microscopy (SEM) studies showed that the samples annealed at 900 °C were clean and uniform in thickness. A thickness of 800 × 1015 atoms/cm2 was determined by ion scattering. Films annealed to 1250 °C likewise showed a continuous unbroken boron nitride layer, but also exhibited morphological features resulting from reactions of the underlying silicon oxide-silicon interface in the substrate. Auger electron spectroscopy and atomic force microscopy showed that the BN coating produced at this higher temperature remained unbroken but had a surface area of ∼15% covered by dimples 2–7 nm in depth. Compared to typical films made by chemical vapor deposition, BN films produced from this “single-source” method have lower hydrogen and carbon concentrations.
Publisher
Springer Science and Business Media LLC
Subject
Mechanical Engineering,Mechanics of Materials,Condensed Matter Physics,General Materials Science
Cited by
23 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献