Gold in Flux-less Bonding: Noble or not Noble

Author:

Balucani Marco,Nenzi Paolo,Palma Fabrizio,Bandarenka Hanna,Dolgyi Leonid,Shapel Aliksandr

Abstract

ABSTRACTThis work highlights the solder joints reliability issues emerged during the development of a novel compliant contacting technology. The peculiar process in this technology is a mechanical lifting procedure in which a pulling force is exerted onto 63Sn-37Pb (eutectic) solder joints (realized by a flux-less thermo compression process), releasing metal traces from the substrate, to form free standing vertical structures. Since joints mechanical characteristics are critical for the successful fabrication of contacts, different bonding conditions (inert or forming atmosphere, temperature rates) and surface finishing (electroplated gold and preformed solder) have been tested. SEM and EDX analyses have been performed on failing joints to investigate failure causes and classify defect typologies. A constantly higher failure rate (percent number of failing joints) has been observed on gold finished surfaces. Analyses proved that such unusual rate was due to contamination of gold surface left by additives in the plating bath and to the embrittlement caused by gold diffusion into molten solder. Plating additives contamination reduces the wettability of gold surfaces. Concentration values of 3 wt.% for gold, considered safe for surface mount applications, caused embrittlement in solder bumps of 20-40 μm diameters.

Publisher

Springer Science and Business Media LLC

Subject

General Engineering

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3