Combined surface characterization and tribological (friction and wear) studies of CVD diamond films

Author:

Perry Scott S.,Ager Joel W.,Somorjai Gabor A.

Abstract

The tribological properties of polycrystalline chemically vapor deposited (CVD) diamond films grown on silicon substrates and containing varying amounts of amorphous carbon impurities were investigated. Films were characterized by secondary electron microscopy (SEM) and atomic force microscopy (AFM) for surface morphology and roughness and by spatially resolved Raman spectroscopy for amorphous carbon (a-C) content. Friction measurements were performed with a Rockwell C hemispherical diamond tip in ultrahigh vacuum (UHV) and in ambient air. In vacuum, the friction coefficient rises monotonically from 0.6 in a region with substantial a-C to 0.85 in a region with pure diamond. Under ambient conditions, the friction coefficient is substantially lower than that in vacuum and deceases slightly (from ∼0.19 to ∼0.16) with the decreasing a-C content. Under both vacuum and ambient conditions, the friction coefficient was observed to be independent of load over the range of 0.1–0.5 N. The friction values are discussed in terms of adhesion between the diamond tip and the film. Qualitative scratch hardness measurements were performed in UHV by measuring the minimum load at which plastic deformation occurs for a single traversal of the tip. Scratch hardness is found to increase with increasing diamond content of the films. The wear mechanism of the pure diamond regions was evaluated by examining wear tracks with SEM and AFM. The wear tracks showed evidence of spalling, buckling, and grain pull-out indicative of a cohesive mode of failure (failure at grain boundaries). A decrease in surface roughness in the wear tracks indicates asperity wear. Adhesive failure at the Si substrate interface or of a phase transformation of the diamond film was not observed in this load regime.

Publisher

Springer Science and Business Media LLC

Subject

Mechanical Engineering,Mechanics of Materials,Condensed Matter Physics,General Materials Science

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3