Effects of substrate on determination of hardness of thin films by nanoscratch and nanoindentation techniques

Author:

Tayebi Noureddine,Polycarpou Andreas A.,Conry Thomas F.

Abstract

A comparative study on the effects of the substrate on the determination of hardness of thin films by the use of the nanoscratch and nanoindentation techniques was conducted. Gold films deposited on fused quartz substrates and silicon dioxide films deposited on aluminum substrates with variant film thicknesses were investigated. These two systems correspond to a soft film on a hard substrate and a hard film on a soft substrate, respectively. The effect of substrate interaction on the measurement of hardness using the nanoscratch technique was found to be less pronounced compared to that of the nanoindentation technique due to: (i) the lower normal loads applied to achieve the penetration depths that occur at higher loads when using the nanoindentation method; (ii) the direct imaging of the residual deformation profile that is used in the nanoscratch technique, which allows for the effects of pileup or sink-in to be taken into account, whereas in the nanoindentation technique the contact area is estimated from the load-displacement data, which does not include such effects; and (iii) the account of elastic recovery of the plastically deformed surfaces from scratch tests. The film thickness did not appear to have any effect on the hardness of Au and SiO2 films obtained from nanoscratch data. This observation allowed, for the case of SiO2 films, the determination of the “free substrate effect region” and the derivation of an empirical relationship that relates the composite hardness of the film/substrate system to the contact-depth-to-film-thickness ratio, even when the indenter penetrates into the substrate. Such findings can allow for the determination of the intrinsic hardness of ultrathin hard films (∼1–5 nm thick), where the substrate effect is unavoidable.

Publisher

Springer Science and Business Media LLC

Subject

Mechanical Engineering,Mechanics of Materials,Condensed Matter Physics,General Materials Science

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3