Observation and Modelling of Electromigration-Induced Void growth in Al-Based Interconnects

Abstract

AbstractAccelerated electromigation tests on unpassivated, pure aluminum interconnects were performed. The failure mechanisms were observed by interrupting the tests and exanming the conductor lines using an SEM. Because the metal thin film was subjected to a so-called laser reflow process before patterning, grain boundaries were visible in the SEM as thermal grooves. Voids were observed to move along the line and to grow in a transgranular manner, and a characteristic asymmetric void shape was identified which seems to be related to the failure mechanism. It is argued that substantial progress in modelling and understanding of electromigration failure can be made by consideration of such void shape effects.