Abstract
ABSTRACTThe x-ray reflectivity and surface morphology of C/W multilayers fabricated by ion beam sputtering (IBS) method was evaluated. Also the surface roughness and amorphous structure of C and W films fabricated by direct ion beam deposition (DIBD) method were evaluated as a function of ion energy. The reflectivity was measured by the C-K line (4.47nm) and STM was used for surface roughness measurement and root-mean-square value of correlation function of the RHEED pattern was used for evaluation of amorphous structure. The reflectivity of C/W multilayer was about 69% of the theoretical one, and micro-columnar structures were observed from STM images. The film structure and surface roughness of DIBD film were changed with the depositing ion energy. The surface roughness of films becomes smaller as the depositing energy becomes higher in the energy range from 20 to 140eV.
Publisher
Springer Science and Business Media LLC
Reference5 articles.
1. Performances Of C-W Multilayers As Soft X-Rays Optics : High Reflectivity In The Range 2d = 60 to 100 Å
2. Investigation of Oxide/Metal Multilayers for Soft X-Ray Optics Fabricated by Ion Beam Sputterinc
3. 3. Etoh K. , Kataoka I. , Ito K. Yonemitsu T. , Hoshi N. , Sekiguchi H. , Yamada I. , Delaunay J. and Durand H. , Proceedings of SPIE 1546(1991)
4. Evaluation of Multilayers for Soft X-Ray Fabricated by Ion Beam Sputtering.
5. 5. Ito K. , Yonemitsu T. , Etoh K. , Sekiguchi H. , Yamada I. Kataoka I. and Durand H. , To be published in Nuclear Instruments and Methods, B.(1991).a
Cited by
6 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献