Laser Induced Oxidation Effects in Bismuth Thin Films

Abstract

ABSTRACTThe Laser induced oxidation process of bismuth was investigated using Raman spectroscopy. Upon laser irradiation (λ = 532 nm) pure Bismuth was transformed gradually into Bi2O3. Raman spectra of the samples showed the characteristics peaks for pure Bi located at 71 cm-1 and 96 cm-1. The oxidation process was monitored by Raman spectra with four additional bands located at about 127 cm-1, 241 cm-1, 313 cm-1 and 455 cm-1. Maintaining constant the exposure time of irradiation, the intensity of these bands depended on laser irradiation power. The presence of Bi2O3 in the sample was confirmed through by energy dispersion spectroscopy (EDS).