Electron Beam Induced Decomposition of Palladium Acetate

Abstract

AbstractA focused electron beam has been used to selectively decompose sub micron thick films of palladium acetate, Pd(OOCCH3)2, resulting in the formation of <0.1μm wide Pd rich features. Resistivity of the palladium acetate film decreased when exposed to doses above 500μC/cm2. Annealing to 160°C further reduces the resistivity of the exposed areas to as low as 100μΔcm. XPS analysis of the exposed areas indicate that the Pd is reduced to a metallic state and that the ratio of C and 0 to Pd drops to 1.5 and 0.6, respectively, after exposure. Residual gas analysis during exposure indicates that CO2 and CH3 are the primary volatile products of the decomposition.