Author:
Hong Suk-Kyoung,Yoon Yang Han,Baek Yong Ku,Lee Chang Goo,Suh Chung Won,Lee Seok Won,Kang Young Min,Kang Nam Soo,Hwang Cheol Seong,Kwon Oh Seong
Abstract
The degradation behavior of integrated Pt/SrBi2Ta2O9/Pt capacitors caused by hydrogen impregnation during the spin-on glass (SOG)-based intermetal dielectric (IMD) process was investigated. SOG was tested as an IMD since it offers better planarity for multilevel metallization processes compared to other SiO2 deposition methods. It was found that the SOG itself does not degrade the ferroelectric performance. Deposition of an under-layer of SiOxNy by plasma-enhanced chemical vapor deposition (PECVD) using SiH4 + N2O + N2 source gases and a SiO2?x capping layer by another PECVD process using SiH4 + N2O source gases produced hydrogen as a reaction by-product. The hydrogen diffused into the SBT layer and degraded the ferroelectric performance during subsequent annealing cycles. A very thin (10 nm) Al2O3 layer grown by atomic layer deposition before the IMD process successfully blocked the impregnation of the hydrogen. Therefore, excellent ferroelectric performance of the SBT capacitors were maintained after the multilevel metallization process as well as passivation. The adoption of SOG in the IMD process greatly improved the surface flatness of the wafer resulting in a higher capacitor yield with very good uniformity in ferroelectric properties over the 8-in.-diameter wafer.
Publisher
Springer Science and Business Media LLC
Subject
Mechanical Engineering,Mechanics of Materials,Condensed Matter Physics,General Materials Science
Cited by
4 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献