Glass fibre-reinforced polyphenylene sulphide composites were prepared by hot-pressing glass fibre fabrics and polyphenylene sulphide resins. The effects of different polyphenylene sulphide resin forms on the properties of the composites were investigated using scanning electron microscopy, dynamic mechanical analyser, pendulum impact tester and universal testing machine. The results showed that different polyphenylene sulphide resin forms had nearly no effect on the glass transition temperature of the composites, which are all located at about 100 °C. Compared with other polyphenylene sulphide composites, the bending strength of polyphenylene sulphide film composites was the highest, reaching 314.58 MPa, and the impact strength of polyphenylene sulphide particle composites was the highest, reaching 245.4 KJ/m2. The bending strength and impact strength were calculated using a standard fraction, and the highest standard fraction was obtained when the ratio of polyphenylene sulphide film to particle was 1:2. The impact strength and bending strength could be obtained. The impact strength reached 229.8 KJ/m2, and the bending strength reached 284.16 MPa.
Funder
“Research on Preparation, Mechanical Properties and Biological Adhesion of Basalt Fibre Reinforced Composites for Marine Pasture” of Zhejiang Sci-Tech University Huzhou Research Institute Co.
Subject
General Materials Science
Reference47 articles.
1. Hydrogen sulphide capture and removal technologies: A comprehensive review of recent developments and emerging trends;Pudi;Sep. Purif. Technol.,2022
2. Durability and notch sensitivity analysis of environmental ageing induced glass fibre mat and kenaf fibre mat-reinforced composites;Miah;J. Ind. Text.,2021
3. Bowman, S., Jiang, Q., Memon, H., Qiu, Y., Liu, W., and Wei, Y. Effects of styrene-acrylic sizing on the mechanical properties of carbon fiber thermoplastic towpregs and their composites. Molecules, 2018. 23.
4. Polyphenylene sulphide-modified carbon fibre reinforced high-strength composites via electrophoretic deposition;Won;J. Sci.-Adv. Mater. Dev.,2022
5. Hassan, E.A., Elagib, T.H., Memon, H., Yu, M., and Zhu, S. Surface modification of carbon fibers by grafting peek-nh2 for improving interfacial adhesion with polyetheretherketone. Materials, 2019. 12.
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献