1. Department of Materials Science and Engineering, National Cheng Kung University, Tainan 701, Taiwan
Abstract
Chloride ions contained in the sealing compound currently used in the electronic packaging industry not only interact with intermetallic compounds but also have a serious impact on silver alloy wires. A 15 μm ultrafine quaternary silver-palladium-gold-platinum alloy wire was used in this study. The wire and its bonding were immersed in a 60 °C saturated sodium chloride solution (chlorination experiment), and the strength and elongation before and after chlorination were measured. Finally, the fracture surface and cross-section characteristics were observed using a scanning electron microscope and focused ion microscope. The results revealed that chloride ions invade the wire along the grain boundary, and chlorides have been generated inside the cracks to weaken the strength and elongation of the wire. In addition, chloride ions invade the interface of the wire bonding to erode the aluminum substrate after immersing it for enough long time, causing galvanic corrosion, which in turn causes the bonding joint to separate from the aluminum substrate.
Subject
General Materials Science
Reference28 articles.
1. Study of wire bonding reliability of Ag-Pd-Au alloy wire with flash-gold after chlorination and sulfidation;Wu;Microelectron. Reliab.,2019
2. Chen, K.J., Hung, F.Y., and Chang, C.Y. (2019). A Study of the Sulfidation Behavior on Palladium-Coated Copper Wire with a Flash-Gold Layer (PCA) after Wire Bonding. Electronics, 8.
3. Yang, G., Zhou, Z., Zhang, H., Zhang, Y., Peng, Z., Gong, P., Wang, X., and Cui, C. (2022). Improved Anti-Vulcanization and Bonding Performance of a Silver Alloy Bonding Wire by a Cathodic Passivation Treatment with Palladium. Materials, 15.
4. Manoharan, S., Patel, C., and McCluskey, P. (2017). International Electronic Packaging Technical Conference and Exhibition, 2017 August, 58097, V001T05A004), American Society of Mechanical Engineers.
5. Reliability of Cu wire bonds in microelectronic packages;Khatibi;Microelectron. Reliab.,2017
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献