Abstract
The phase transformation kinetics under continuous cooling conditions for intercritical austenite in a cold rolled low carbon steel were investigated over a wide range of cooling rates (0.1–200 ∘ C/s). The start and finish temperatures of the intercritical austenite transformation were determined by quenching dilatometry and a continuous cooling transformation (CCT) diagram was constructed. The resulting experimental CCT diagram was compared with that calculated via JMatPro software, and verified using electron microscopy and hardness tests. In general, the results reveal that the experimental CCT diagram can be helpful in the design of thermal cycles for the production of different grades of dual-phase–advanced high-strengh steels (DP-AHSS) in continuous processing lines. The results suggest that C enrichment of intercritical austenite as a result of heating in the two phases (ferrite–austenite) region and C partitioning during the formation of pro-eutectoid ferrite on cooling significantly alters the character of subsequent austenite phase transformations.
Subject
General Materials Science,Metals and Alloys
Reference45 articles.
1. Advanced High-Strength Steels Application Guidelines V6;Keeler,2017
2. New cars — new materials
3. Main Features of Heat Treatment from Intercritical Region;Fonstein,2015
4. Evolution of strength of automotive steels to meet customer challenges;Fonstein,2015
5. Effect of austenite dispersion on phase transformation in dual phase steel
Cited by
26 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献