Abstract
Silicalite-1 membrane was prepared on an outer surface of a tubular α-alumina support by a secondary growth method. Changes of defect amount and crystallinity during secondary growth were carefully observed. The defect-less well-crystallized silicalite-1 membrane was obtained after 7-days crystallization at 373 K. The silicalite-1 membrane became (h0l)-orientation with increasing membrane thickness, possibly because the orientation was attributable to “evolutionally selection”. The (h0l)-oriented silicalite-1 membrane showed high p-xylene separation performance for a xylene isomer mixture (o-/m-/p-xylene = 0.4/0.4/0.4 kPa). The p-xylene permeance through the membrane was 6.52 × 10−8 mol m−2 s−1 Pa−1 with separation factors αp/o, αp/m of more than 100 at 373 K. As a result of microscopic analysis, it was suggested that a very thin part in the vicinity of surface played as effective separation layer and could contribute to high permeation performance.
Subject
Inorganic Chemistry,Condensed Matter Physics,General Materials Science,General Chemical Engineering
Cited by
11 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献