Abstract
We have reported a method of fabricating (111)-orientated nanotwinned copper (nt-Cu) by direct current electroplating. X-ray analysis was performed for the samples annealed at 200 to 350 °C for an hour. X-ray diffraction indicates that the (200) signal intensity increases while (111) decreases. Abnormal grain growth normally results from transformation of surface energy or strain energy density. The average grain size increased from 3.8 µm for the as-deposited Cu films to 65–70 µm after the annealing at 250 °C for 1 h. For comparison, no significant grain growth behavior was observed by random Cu film after annealing for an hour. This research shows the potential for its broad electric application in interconnects and three-dimensional integrated circuit (3D IC) packaging.